Recommended Cutting Conditions
4PGSS, 5PGSS
Application Workpiece Material Application Depth of Cut Outside Dia. 3 4 5 6 8 10 12 16 20 25
(apae) (mm) Dc (mm) 6,600 5,000 4,000 3,300 2,500 2,000 1,600
BF 1,320 1,200 1,360 1,320 1,200 1,200 1,360
Shouldering 1D0.3D Spindle Revolution 13,300 10,000 8,000 6,600 5,000 4,000 3,300 2,500 2,000 1,600
(min-1) 660 600 680 660 600 600 680
Slotting Shouldering 1D
Carbon Steel Slotting Feed Rate (mm/min) 1,860 1,600 1,440
SxxC
Spindle Revolution
(min-1)
Feed Rate (mm/min)
Spindle Revolution 10,600 8,000 6,400 5,300 4,000 3,200 2,700 2,000 1,600 1,300
(min-1)
Shouldering 1D0.3D
Alloy Steel Feed Rate (mm/min) 1,180 1,020 920 840 880 890 860 880 830 1,040
SCM, SNCM
BQ Spindle Revolution 5,300 4,000 3,200 2,700 2,000 1,600 1,300
BQ (min-1)
Slotting 0.75D
Feed Rate (mm/min) 420 440 440 430 440 410 520
Spindle Revolution 8,500 6,400 5,100 4,200 3,200 2,500 2,100 1,600 1,300 1,000
(min-1)
Shouldering 1D0.25D
0.5D Feed Rate (mm/min) 710 610 550 500 570 550 580 570 570 700
Pre-hardened steel
NAK, 30~45HRC Spindle Revolution 4,200 3,200 2,500 2,100 1,600 1,300 1,000
(min-1)
Slotting
Feed Rate (mm/min) 250 290 280 290 280 280 350
Spindle Revolution 5,300 4,000 3,200 2,700 2,000 1,600 1,300 1,000 800 600
(min-1) 240 270
Shouldering 1D0.25D 800 600
Stainless steel Slotting 0.4D Feed Rate (mm/min) 290 250 230 210 240 250 230 240 120 130
SUS
Spindle Revolution 2,700 2,000 1,600 1,300 1,000
(min-1)
Feed Rate (mm/min) 100 120 120 120 120
Spindle Revolution 3,700 2,800 2,200 1,900 1,400 1,100 900 700 550 450
(min-1)
Shouldering 1D0.2D
Titanium Alloys Feed Rate (mm/min) 160 130 110 110 110 130 120 140 130 150
Heat-resistant Alloys Spindle Revolution 1,900 1,400 1,100 900 700 550 450
(40~50HRC) (min-1)
0.3D
Slotting
Feed Rate (mm/min) 60 60 60 60 70 70 80
* Cutting with coolant is recommended for stainless steel, titanium alloys and heat-resistant alloys.
L 4PGSM, 5PGSM, 6PGSM
Application Workpiece Material Application Depth of Cut Outside Dia. 6 8 10 12 16 20 25
(apae) (mm) Dc (mm)
Solid End Mill Carbon Steel Shouldering 1.5D0.3D Spindle Revolution 6,600 5,000 4,000 3,300 2,500 2,000 1,600
SxxC Slotting 0.5D (min-1) 1,030 980 1,260 1,520 1,570 1,510 1,340
BQ 6,600 5,000 4,000 3,300 2,500 2,000 1,600
Feed Rate (mm/min) 520 500 640 770 790 750 670
Spindle Revolution
(min-1)
Feed Rate (mm/min)
Alloy Steel Shouldering 1.5D0.3D Spindle Revolution 5,300 4,000 3,200 2,700 2,000 1,600 1,300
SCM, SNCM Slotting 0.5D (min-1) 740 670 940 1,130 1,170 1,140 1,030
5,300 4,000 3,200 2,700 2,000 1,600 1,300
BF Shouldring 1.5D0.2D Feed Rate (mm/min) 380 330 480 560 580 570 520
Shouldering 0.4D Spindle Revolution 4,200 3,200 2,500 2,100 1,600 1,300 1,000
Pre-hardened steel 470 490 610 700 730 710 710
NAK, 30 45HRC (min-1) 4,200 3,200 2,500 2,100 1,600 1,300 1,000
Feed Rate (mm/min) 230 250 310 350 370 350 360
Slotting Spindle Revolution
(min-1)
Feed Rate (mm/min)
Spindle Revolution
(min-1)
Feed Rate (mm/min)
BQ Stainless steel Shouldering 1.5D0.2D Spindle Revolution 2,700 2,000 1,600 1,300 1,000 800 600
SUS Slotting 0.4D (min-1) 170 190 250 280 280 280 250
2,700 2,000 1,600 1,300 1,000 800 600
Feed Rate (mm/min) 80 90 120 140 140 140 130
Spindle Revolution
(min-1)
Feed Rate (mm/min)
Slotting Spindle Revolution 1,900 1,400 1,100 900 700 550 450
(min-1)
Shouldering 1.5D0.2D
Titanium Alloys Feed Rate (mm/min) 90 90 130 150 160 150 150
Heat-resistant Alloys Spindle Revolution
(min-1)
(40~50HRC) 1,900 1,400 1,100 900 700 550 450
Slotting 0.3D
Feed Rate (mm/min) 40 40 60 70 80 70 70
* Cutting with coolant is recommended for stainless steel, titanium alloys and heat-resistant alloys.